Research on Performance of Rubberized Concrete Incorporated with Polymer

  • YANG Ruo-chong1, TAN Zhi-ming2, HUANG Xiao-ming1, MA Yi-ping3
Author information +
文章历史 +

摘要

为研究聚合物对橡胶混凝土性能的改善作用,比较了不同橡胶掺量的聚合物改性混凝土路用性能。通过密度、抗折强度、抗压强度及劈裂强度试验,分析了掺聚合物的橡胶混凝土基本力学性能及物性的变化规律,并通过冲击试验分析了混凝土的抗冲击韧性;参照混凝土抗折强度试验方法,研究了掺聚合物的橡胶混凝土的粘结性能;采用噪声仪及超声波仪分析了橡胶混凝土的减振降噪效果。结果表明:替代粗集料的橡胶体积分数不超过30%时,可获得路用性能及减振降噪效果较优的橡胶混凝土路面材料。

Abstract

In order to study performance improvement effect of rubberized concrete incorporated with polymer, pavement performances of polymer modified concrete with volume fractions of different rubber particles were compared. Through tests of density, flexural strength, compressive strength, indirect tensile strength of rubberized concrete, variation laws of basic mechanical properties and physical characteristics of rubberized concrete with polymer were studied. Impact toughness of rubberized concrete by impact test was analyzed. Referred to the experiment method of flexural strength of concrete, bonding performance of rubberized concrete with polymer was investigated.Through noise instrument and ultrasonic instrument, vibration and noise reduction effects of rubberized concrete were studied. The results show that when volume fraction of rubber particles does not exceed 30 percent of aggregate, the excellent pavement performance and the effect of noise reduction of rubberized concrete for concrete pavement material can be attained.

关键词

道路工程 / 橡胶混凝土 / 试验研究 / 聚合物 / 路用性能

Key words

road engineering / rubberized concrete / experimental research / polymer / pavement performance

引用本文

导出引用
杨若冲,谈至明,黄晓明,马一平. 掺聚合物的橡胶混凝土路用性能研究[J]. 中国公路学报, 2010, 23(4): 15-19
YANG Ruo-chong, TAN Zhi-ming, HUANG Xiao-ming, MA Yi-ping. Research on Performance of Rubberized Concrete Incorporated with Polymer[J]. China Journal of Highway and Transport, 2010, 23(4): 15-19
中图分类号: U416.218   

参考文献

[1] SEGRE N,JOEKES I.Use of Tire Rubber Particles as Addition to Cement Paste[J].Cement and Concrete Research,2000,30(9):1421-1425.
[2]KHATIB Z K,BAYOMY F M.Rubberized Portland Cement Concrete[J].Journal of Materials in Civil Engineering,1999,11(3):206-213.
[3]ZHENG L,SHARON H X,YUAN Y.Experimental Investigation on Dynamic Properties of Rubberized Concrete[J].Construction and Building Materials,2008,22(5):939-947.
[4]HAN Zhu.Rubber Crumbs in Concrete[J].Cement and Concrete Research,2002,32(10):1587-1596.
[5]TAHA M M R,EL-DIEB A S,ABD EL-WAHAB M A,et al.Mechanical, Fracture, and Microstructural Investigations of Rubber Concrete[J].Journal of Materials in Civil Engineering,2008,20(10):640-649.
[6]SIDDIQUE R,NAIK T R.Properties of Concrete Containing Scrap-tire Rubber-an Overview[J].Waste Management,2004,24(6):563-569.
[7]李 悦,XI Yun-ping.橡胶集料水泥砂浆和混凝土的性能研究[J].混凝土,2006(6):45-48.
LI Yue,XI Yun-ping.Study on the Properties of Portland Cement Mortar and Concrete Containing Crumb Rubber Aggregate[J].Concrete,2006(6):45-48.
[8]陈 波,张亚梅,陈胜霞,等.橡胶混凝土性能的初步研究[J].混凝土,2004(12):37-39.
CHEN Bo,ZHANG Ya-mei,CHEN Sheng-xia,et al.Fundamental Research of Properties of Rubberized Concretes[J].Concrete,2004(12):37-39.
[9]SAVAS B Z,AHMAD S,FEDROFF D.Freeze-thaw Durability of Concrete with Ground Waste Tire Rubber[J].Transportation Research Record,1997(1574):80-88.
[10]李红燕.橡胶改性水泥基材料的性能研究[D].南京:东南大学,2004.
LI Hong-yan.The Properties of Cement Based Ma-terials Containing Rubber[D].Nanjing:Southeast University,2004.

基金

上海市科学技术委员会科研计划项目(052012001)
PDF全文下载(590 KB)

1310

Accesses

0

Citation

Detail

段落导航
相关文章

/